Reactive Emulsifiers
➣tip2: Phosphate emulsifiers can obtain stable emulsion,and also have good
dispersion.
➣tip3: Aggolomerate and oligomers maybe occur when adding quickly or under
high-temperature.
➣tip4: High dosage is beneficial to improve the water-resistance of the film.
Products Detail
reactive surfactant | Ionic pattern | Chemical name | Solid fraction(WT%) | Critical micelle concentration(%) | Surface tension(mN/m) | 无APEO | Characteristic |
AE-100 | Nonionic | Allyl polyether | 99%min | - | - | √ |
Reactive active group, copolymerized with acrylic monomers Excellent solubility and dispersibility It can emulsify monomers (except AE-100) and has good compatibility with high electrolyte. Improving the ability of emulsion to resist calcium chloride Hydrophilic Modification by Solvent Copolymerization |
AE-200 | Nonionic | Polyether Containing Double Bond Groups | 99%min | - | - | ||
AE-300 | Nonionic | Polyether Containing Double Bond GroupsEO=10 | 99%min | - | - | √ | |
AE-320 | Nonionic | Polyether Containing Double Bond GroupsEO=20 | 98%min | - | - | √ | |
AE-3218 | Nonionic | Polyether Containing Double Bond GroupsEO=20 | 17.5-18.5% | 0.15-0.2 | 41.6 | √ | |
AE-330 | Nonionic | Polyether Containing Double Bond GroupsEO=30 | 98%min | - | - | √ | |
APE-2003 | anion | Acrylic polyether phosphate | 98%min | - | - | √ |
Copolymer monomers to enhance the flexibility and cohesion of coatings Characteristic of phosphoric acid group, excellent dispersibility of pigments and fillers, good adhesion of substrates It can improve the hydrolytic stability of emulsion system. Improving waterproofing and scrubbing resistance |
APE-2005 | anion | Methacrylic acid polyether phosphate | 98%min | - | - | √ | |
APE-2012 | anion | Alcohol ether phosphate containing double bonds | 96% min | - | - | √ | |
A-2404 | anion | Methacrylamide isopropyl sulfonic acid | 98%min | - | - | √ | It can not emulsify monomer, improve waterproof and scrubbing properties, improve pigment acceptability, and improve adhesion. It can improve mechanical stability and hydrolytic stability of emulsion system. |
A-2405NA | anion | Sodium methacrylamide isopropyl sulfonate | 48-51% | - | - | √ | |
A-2405NH | anion | Ammonium methacrylamide isopropyl sulfonate | 48-51% | - | - | √ | |
NRS-10 | anion | Alkyl alcohol ether sulfate containing allyl group | 49-51% | 0.08-0.15 | 36 | √ |
Emulsifying monomer Low active agent dosage in emulsification(1—3%max) Solid content of high emulsion (above 50%) Excellent mechanical stability Give the emulsion good water resistance, in which NRS-1225 has longer alkyl chain than NRS-1025 and M-12S than M-10S, and finer particle size. |
NRS-1025 | anion | Alkyl alcohol ether sulfate containing allyl group | 24-26% | 0.08-0.15 | 36 | √ | |
NRS-1230 | anion | Alkyl alcohol ether sulfate containing double bond group | 24-26% | 0.025-0.075 | 40.9 | √ | |
NRS-138 | anion | Dialkyl sulfosuccinate salts containing double bonds | 39-42% | 0.1-0.2 | 31 | √ | |
NRS-320 | anion | Dialkyl sulfosuccinate salts containing double bonds | 24-26% | 0.05-0.1 | 27.3 | √ | |
M-10S | anion | Dialkyl sulfosuccinate salts containing allyl group | 49-52% | 0.05-0.08 | 27.1 | √ | |
M-12S | anion | Alkyl Sulfosuccinate Salts Containing Allyl Group | 39-42% | 0.075-0.1 | 29.8 | √ | |
M-16S(new) | anion | Alkyl Alcohol Ether Sulfosuccinate Diester Sodium Salt Containing Allyl Group | 39-42% | 0.05-0.1 | 33.5 | √ | |
M-20S | anion | Dialkyl sulfosuccinate salts containing double bonds | 37-39% | 0.025-0.075 | 26.9 | √ | |
M-30S | anion | Dialkyl sulfosuccinate salts containing double bonds | 49-51% | 0.025-0.05 | 25 | √ | |
SVS | anion | Vinyl sulfonate | 33-37% | - | - | √ | Improving the stability of emulsion by comonomer |
UCAN-1 | anion | Sodium 1-propoxy 2-hydroxypropane sulfonate | 41-44% | - | - | √ | Improve the waterproof and scrubbing properties of the paint film, improve the stability of the emulsion and reduce the gel amount during the polymerization process. |
UCAN-3 | anion | Alcohol ether phosphate containing double bonds | 39-41% | - | - | √ |
It can copolymerize with vinyl acetate, styrene and acrylic monomers to improve the waterproof and scrubbing resistance of the paint film, the acceptance of the pigment and the adhesion. It can improve the mechanical stability, hydrolytic stability of the emulsion system, and reduce the gel amount of polymerization process. |
UCAN-4 | anion | Specially made Alcohol ether phosphate containing double bonds | 39-41% | - | - | √ | |
V-10S | anion | Ammonium polyether sulfate containing double bond group | 49-52% | - | - | √ | Give the emulsion excellent stability, so that the emulsion coating has good water resistance and copolymerization properties. |
V-20S | anion | Polyether sulfate containing allyl alkoxy group | 49-52% | 0.025-0.06 | 40 | The emulsion has excellent emulsifying ability and gives excellent stability to the emulsion. The emulsion film has good water resistance and excellent copolymerization properties, resulting in extremely low APEO content. V-1025S has good polymerization performance with styrene-containing monomers. | |
V-1025S | anion | Alkyl propylene phenoxy polyether sulfate | 24-26% | 0.05-0.15 | 38.9 | ||
V-100P | anion | Allyl polyether phosphate | 99% | 0.1-0.2 | 33 | √ | It has good solubility and dispersibility, & nbsp; can be grafted onto the polymer chain in the reaction, thus forming a unique dispersion protection structure. |
V-200P | anion | Ammonium polyether phosphate containing double bonds | 98% | 0.02-0.08 | 35 |
Anionic emulsifier without APEO