  • 产品名称: Reactive Emulsifiers
  • tip1: Mixture ratio of prepolymer and emulsifier can be at 5:1.
  • tip2: Phosphate emulsifiers can obtain stable emulsion,and also have good dispersion.
  • tip3: Aggolomerate and oligomers maybe occur when adding quickly or under high-temperature.
  • tip4: High dosage is beneficial to improve the water-resistance of the film.

Products name Chemical name Ion type Solid content(WT%) Critical micelle concentration     (%) Surface tension(mN/m) APEO free Characteristics
AE-100 Allyl polyether Non-ionic 99%min - - 1/Can be used in the copolymerization of acrylic monomers with reactive groups.
2/Excellent solubility and dispersion performance.
3/Can emulsify monomers, good compatibility with high electrolyte.
4/Improve chemical stability.
5/Solvent copolymerization for hydrophilic modification(Except AE-3218).
AE-200 Polyether containing double bond Non-ionic 99%min - -  
AE-300 Polyether containing double bondEO=10 Non-ionic 99%min - -
AE-320 Polyether containing double bondEO=20 Non-ionic 98%min - -
AE-3218 Polyether containing double bondEO=20 Non-ionic 17.5-18.5% 0.15-0.20 41.6
AE-330 Polyether containing double bondEO=30 Non-ionic 98%min - -
APE-2003 Acrylic acid polyether phosphate Anion 98%min - - 1/Copolymerized monomer, enhance flexibility.
2/Contain phosphate,excellent dispersibility for pigments and adhesion to the substrate.
3/Can enhance hydrolytic stability of the emulsion system.
4/Improve the waterproof performance and scrub resistance.
APE-2005 Methacrylic acid polyether phosphate Anion 98%min - -
APE-2012 Polyether phosphate containing double bond Anion 96% min - -
A-2404 Methyl acrylamide isopropyl sulfonic acid Anion 98%min - - 1/Can't emulsify monomers. 
2/Can improve the waterproof performance and scrub resistance.
3/Improve the pigment capacity,adhesion,the mechanical stability and hydrolytic stability of the emulsion system.
A-2405NA Methyl acrylamide isopropyl sodium sulfonate Anion 48-51% - -
A-2405NH Methyl acrylamide isopropyl ammonium sulfonate Anion 48-51% - -
NRS-10 Alcohol ether sulfate containing allyl Anion 49-51% 0.08-0.15 36 1/Can emulsify monomers.
2/Low dosage when emulsification (1-3%max).
3/High solid content of emulsion (more than 50%).
4/Excellent mechanical stability.
5/Endowed emulsion with good water resistance.                                                              6/Alkyl chain of M-12S is longer than M-10S,and with finer particle size.
NRS-1025 Alcohol ether sulfate containing allyl Anion 24-26% 0.08-0.15 36
NRS-1230 Alcohol ether sulfate containing allyl Anion 24-26% 0.025-0.075 40.9
NRS-138 Dialkyl sulfosuccinate ester salt containing double bond Anion 39-42% 0.1-0.2 31
NRS-320 Dialkyl sulfosuccinate ester salt containing double bond Anion 24-26% 0.05-0.1 27.3
M-10S Dialkyl sulfosuccinate ester salt containing double bond Anion 49-52% 0.05-0.08 27.1
M-12S Alkyl sulfosuccinate diester sodium salt containing allyl Anion 39-42% 0.075 29.8
M-16S(New) Alkyl sulfosuccinate diester sodium salt containing allyl Anion 39-42% 0.05-0.1 33.5
M-20S Dialkyl sulfosuccinate ester salt containing double bond Anion 37-39% 0.025-0.075 26.9
M-30S Dialkyl sulfosuccinate ester salt containing double bond Anion 49-51% 0.025-0.05 25
SVS Vinyl sulfonate Anion 33-37% - - Comonomer, improve the stability of the emulsion.
UCAN-1 1-propylene oxygen-2- hydroxyl propane sodium sulfonate Anion 41-44% - - 1/Improve the waterproof performance and scrub resistance of paint film.     2/Improve the stability of the emulsion and reduce the amount of gel in polymerization.
UCAN-3 Alkyl acohol polyoxyethylene ether phosphate containing double bond Anion 39-41% - - 1/Copolymerize with vinyl acetate,styrene and acrylic monomers.
2/Improve the waterproof performance and scrub resistance of paint film, enhance acceptance and adhesion of the pigment.
3/It can improve the mechanical stability and hydrolytic stability of emulsion system,reduce gel content in polymerization.
UCAN-4 Alkyl acohol polyoxyethylene ether phosphate containing double bond Anion 39-41%  - -
V-10S Polyether ammonium sulfate containing double bond Anion 49-52% - - 1/Endow the emulsion with excellent stability, make the emulsion film has good water resistance.
2/Copolymerization make the emulsion has good stability.
V-20S Polyether sulfate containing allyl alkoxy Anion 49-52% 0.025-0.06 40   1/Have excellent emulsion performance.2/With excellent emulsion stability, make the emulsion film has good water resistance.3/Excellent copolymeration, make the content of APEO very low.4/V-1025S has excellent polymerization with styrene monomer.
V-1025S Alkyl allyl phenoxy polyether sulfate Anion 24-26% 0.05-0.15 38.9  
V-100P Allyl polyether phosphate Anion 99% 0.1-0.2 33 Has good solubility and dispersibility, can be grafted to the polymer chain in the reaction,and form the unique structure of  dispersed protection.
V-200P Polyether ammonium phosphate containing double bond Anion 98% 0.02-0.08 35  